Home » HI-WAX™ Polyethylene Wax Applications
HI-WAX™ Polyethylene Wax Applications

The various grades of HI-WAX™ are used for a broad range of applications, such as slip agents, disperants, resin modifiers, and mold release agents for the molding of various synthetic resins.

 

Mold Release Agent for the Molding of Plastics

The polyethylene wax can be used as a mold release agent for plastics due to its releasability which increases productivity, prevents pollution and enables the molding of complex shapes.

image

 

Modifier for Engineered Plastics

It is used as a modifier for engineered plastics due to its impact strength and flexural modulus properties. With the use of HI-WAX™, manufacturers realize cost reduction due to thin materials.

image

 

 

image

 

Release Agent for Rubbers

HI-WAX™ can also be used as a release agent for rubbers due to its releasability and stability.

image

 

Dispersant for Color Masterbatch

Two grades of HI-WAX™ are available for dispersant for color masterbatch applications; HI-WAX™ 420P which is a conventional type wax, and HI-WAX™ GB-01 which is a slightly acid modified type wax. Advantages of HI-WAX™ 420P include good pigment dispersibility, cost-effectiveness, and meets food regulations. For HI-WAX™ GB-01, advantages include special molecular design for and better pigment dispersibility.

 image

Physical Properties for Pigment Dispersant

Optimized Molecular Design for Pigment Dispersant

Evaluation for Color Masterbatch

Pigment Dispersibility of Cast Films

 

 

 

 

 

Related Products

ADMER™ Adhesive Resin

Polyolefin based tie-layer resin that bonds dissimilar polymers for multilayer barrier structures.

CHEMIPEARL™ Polyolefin-based Aqueous Dispersion

Aqueous dispersion of polyolefin fine particles with no emulsifying agents or organic solvents, used as printing ink additives, heat sealing for food packaging, adhesives and binders, and anti-blocking agents.

EXCEREX™ Olefin Oligomer

A narrow molecular weight distribution olefin oligomer used as a polymer processing aid, reduces torque in the extruder and allows for an increase in screw speed while operating at a lower barrel temperature.

TAFMER Polyolefin Elastomers

Low-crystallinity copolymer modifies polyethylene (PE) and polypropylene (PP) offering softness, improved impact resistance and lower melting point.

Back to Top