EXCEREX™ Olefin Oligomer Applications

Applications

Application examples as a molding improvement agent

(1) PP extrusion molding (0.5mm-thick sheet)
By adding 3% EXCEREX ™ 30200BT, extrusion volume was increased from 20kg/h to 40kg/h.

(2) PP extrusion molding (0.5mm-thick sheet)
By adding 3% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 230°C to 210°C and scorching was reduced.

(3) EVA-LDPE blend extrusion molding (0.5mm-thick sheet)
By adding 2% EXCEREX ™ 30200BT, extrusion volume increased from 350kg/h to 430kg/h.

(4) L-LDPE inflation molding
By adding 2% EXCEREX ™ 30200BT, screw revolution was increased by 20%, and extrusion volume was increased from 31kg/h to 38kg/h.

(5) Biaxial drawing PP film
By adding 1% EXCEREX ™ 30200BT, screw revolution was increased from 51rpm to 62rpm, and extrusion volume was increased by 20%.

(6) HDPE blow molding (20L poly tank)
By adding 1% EXCEREX ™ 40800T, set cylinder temperature was lowered from 170°C to 150°C, and productivity was improved by 20% by reducing cooling time from 90 seconds to 75 seconds.

(7) PP blow molding (1.5L bottle)
By adding 2% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 190°C to 170°C, and productivity was improved by 14% from 144 units/h to 164 units/h by reducing cooling time from 25 seconds to 22 seconds.

(8) HDPE injection molding (bottle cap)
By adding 3% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 200°C to 180°C thereby reducing scorching.


Examples of the customer's applications

image

 

 

Related Products

APEL™ Cyclo Olefin Copolymer (COC)

High refractive index, low birefringence, optical grade amorphous polyolefin.

HI-WAX™ Polyethylene Wax

A polymerized polyolefin wax used as slip agents, pigment dispersants, modifiers for ink, paints and resins, and as mold release agents for the molding of various synthetic resins.

LUBMER™ High Molecular Weight Polyethylene

High Molecular Weight Polyethylene (HMWPE) for sound deadening of electronic office equipment and for sliding parts in automotive and electronic components.

LUCANT™ Hydrocarbon Based Synthetic Oil

As a base oil, or a viscosity modifier, improves lubricants that are required to have heat resistance, low-temperature resistance and high shear stability. As an additive to rubber, resins, paints and coatings, improves processability, flexibility, heat resistance, low-temperature properties, sliding properties and defoaming properties.

MIPELON™ Fine Particle Ultra High Molecular Weight Polyethylene Powder (UHMWPE Powder)

Lubricity additive for coatings, and compounding of rubber and engineering plastics, and a sintering resin for filter media.

Back to Top