Application examples as a molding improvement agent

(1) PP extrusion molding (0.5mm-thick sheet)
By adding 3% EXCEREX ™ 30200BT, extrusion volume was increased from 20kg/h to 40kg/h.

(2) PP extrusion molding (0.5mm-thick sheet)
By adding 3% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 230°C to 210°C and scorching was reduced.

(3) EVA-LDPE blend extrusion molding (0.5mm-thick sheet)
By adding 2% EXCEREX ™ 30200BT, extrusion volume increased from 350kg/h to 430kg/h.

(4) L-LDPE inflation molding
By adding 2% EXCEREX ™ 30200BT, screw revolution was increased by 20%, and extrusion volume was increased from 31kg/h to 38kg/h.

(5) Biaxial drawing PP film
By adding 1% EXCEREX ™ 30200BT, screw revolution was increased from 51rpm to 62rpm, and extrusion volume was increased by 20%.

(6) HDPE blow molding (20L poly tank)
By adding 1% EXCEREX ™ 40800T, set cylinder temperature was lowered from 170°C to 150°C, and productivity was improved by 20% by reducing cooling time from 90 seconds to 75 seconds.

(7) PP blow molding (1.5L bottle)
By adding 2% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 190°C to 170°C, and productivity was improved by 14% from 144 units/h to 164 units/h by reducing cooling time from 25 seconds to 22 seconds.

(8) HDPE injection molding (bottle cap)
By adding 3% EXCEREX ™ 30200BT, set cylinder temperature was lowered from 200°C to 180°C thereby reducing scorching.

Examples of the customer's applications